MR. JO Lami-LV
Original price was: ₹1,100.00.₹968.00Current price is: ₹968.00. Inclusive of all taxes
Two component low viscosity epoxy lamination system compatible with carbon fiber, glass fiber and chopped strand mat (CSM).
- Description
- Properties
- Applications
- How To Use
- Technical Data Sheet(TDS)
- FAQs
Description
MR. JO Lami-LV is a two-component epoxy with low viscosity. It is ideal for laminating metal models and electrical parts. Additionally, you can use it with carbon fiber, glass fiber, and chopped strand mat (CSM). The resin flows smoothly and bonds strongly. It also lasts a long time. Since it has no solvents, it keeps your workspace clean and safe. Overall, use it for lamination, electrical applications, or composite work.
- Color: Clear
- Pot life @25°C: 100-150mins
- Mixing Ratio: 100:10 PBW
- Mixture consistency: Low Viscous liquid
- Optics: Transparent
- Glass fiber laminates
- Lamination tools
- Composites
- Surfaces should be freed from laitance and dust by sand-blasting. In case sandblasting is not possible, thorough abrading with a hard wire brush should be preferable.
- Suitable degreasing agent should be used to remove any grease, oil or traces on the surface
- Take small quantities of laminating resin and hardener parts by weight as recommended. • Mix the two components together thoroughly for at least 2 minutes so as to achieve uniform mixing and thorough consistency of the mix. Lay the 100-650 gsm of glass fiber/carbon fiber on the surface to be covered, apply 2 or 3 coats of the mixture again. The laminating resin can be poured directly from the mixing can onto the fiberglass/carbon fiber and spread around with the paint roller/brush. • Allow it to cure for the given cure time to get the desired results. • Apply casting system
A1. MR. JO Lami – LV is a low-viscosity, room-temperature curing epoxy resin system for:
- Carbon fiber lamination
- Glass fiber (GF) lay-ups
- Chopped strand mat applications
- Moulded composite structures and repair laminates
A2. Yes. It is specially formulated for manual wetting of fabrics and smooth application over layers, ensuring air release and fiber wet-through.
Q3. What is the mix ratio?A3. Mix 100:10 by weight (resin : hardener). Precise measurement is key to proper cure and mechanical performance.
Q4. Can it be used for carbon fiber composites?A4. Absolutely. It is ideal for both aesthetic carbon finishes and structural laminates, offering excellent fiber wetting and clarity.
Q5. Is it suitable for vacuum bagging or infusion?A5. It is mainly intended for hand lay-up, but with proper adjustments, it can also work in basic vacuum-assisted layups.
Q6. How should the surface be prepared before applying MR. JO Lami – LV?A6.
- Clean, dry, and abrade the substrate
- Ensure no dust, oil, or contaminants
- Pre-coat absorbent surfaces if needed to prevent air entrapment
A7.
- Pot life: ~30–40 minutes at 25°C
- Gel time: ~2–3 hours depending on thickness
- Full cure: ~24 hours
A8. Typically 2–3 layers depending on application speed and area. Mix fresh batches for more extensive laminates.
Q9. Can MR. JO Lami – LV be tinted or pigmented?A9. Yes, use only epoxy-compatible pigments or translucent tints if color modification is needed.
Q10. Can I use it as a clear coat too?A10. It’s designed for structural wet-out, not high-gloss topcoats. For finishes, a dedicated clear topcoat or polishing is recommended.
Q11. How strong is the cured laminate?A11. It cures to a tough, chemical-resistant, and durable composite, offering good bonding between fibers and base.
Q12. Can it be sanded or machined after curing?A12. Yes. It can be sanded, drilled, or shaped once fully cured.
Q13. Does it yellow over time?A13. As with most epoxies, some yellowing may occur over long exposure to UV. Apply a UV-resistant coating for protection.
Q14. Can MR. JO Lami – LV be used outdoors?A14. Yes, for structural use. For aesthetic or exposed applications, UV topcoats are recommended.
Q15. How should I store it?A15.
- Keep in sealed containers
- Store in a cool, dry place
- Shelf life: 12 months unopened